Product Introduction:
With the development of automobile, tractor manufacturing industry and large-scale mining equipment, the size and weight of heat-treated parts are increasing. In order to improve production efficiency, the quenching amount of primary parts is increasing, and continuous quenching automatic line is emerging, which leads to the development of high speed quenching oil. Fast quenching oil is quenching oil with additives added, and the cooling speed is faster than ordinary quenching oil.
Kerun's fast quenching oil has strong cooling capacity, high temperature cooling speed and moderate low temperature cooling speed, which can not only make the workpieces obtain high and uniform surface hardness and enough hardening layer depth, but also can better control the quenching deformation, and the surface of the workpieces after quenching is easy to clean, with good thermal oxidation stability and long service life. KR238 fast and bright quenching oil, with high cooling speed and stable performance, is especially suitable for quenching large module gear, large section bearing ring, bearing roller, textile workpieces, sewing machine workpieces, hardware tools and other workpieces under protective or controlled atmosphere conditions.
Product Features:
1.Short vapor film stage, fast cooling at high and medium temperature stage, and has an appropriate cooling at low temperature stage.
2.For medium and large workpieces, high and uniform surface hardness and enough hardened depth can be obtained, and the deformation of workpiece can also be well controlled.
3.Good thermal oxidation stability, which can maintain long-term stable cooling characteristics and long service life.
4.Good brightness, low oil consumption and low use cost.
Product Parameter:
| Item |
KR238 |
Method |
Method |
| Moisture, ≤ |
0.03% |
GB/T 1133 |
ASTM D6304 |
| Flash point (open cup), ≥ |
190°C |
GB/T 3536 |
ASTM D92 |
| Kinematic viscosity (40°C) |
28-40 mm2/s |
ASTM D7279 |
ASTM D7279 |
| Corrosion (Copper sheet 100°C×3h), ≤ |
1 |
GB/T 5096 |
ASTM D130 |
| Thermal oxidation stability, viscosity ratio, ≤ |
1.25 |
SH/T 0219 |
SH/T 0219 |
| Cooling performance Characteristic temperature |
≥680°C |
GB/T30823 |
ISO 9950 |
| 60°C, static Max. typical cooling rate |
85°C /s |